Trinseo Gpps Styron 634
| Density (23°C): | 1.04 G/cm³ |
|---|---|
| Melt Flow Rate (MFR) (200°C/5.0 Kg): | 3.5 G/10 Min |
| Notched Izod Impact (23°C: | 23 J/m |
VIDEO
Styron™ 666h Trinseo Polystyrene, General Purpose Gpps
| Density (23°C): | 1.04 G/cm³ |
|---|---|
| Melt Flow Rate (MFR) (200°C/5.0 Kg): | 8 G/10 Min |
| Notched Izod Impact (23°C: | 16 J/m |
VIDEO
ABS Chimei Polylac Pa-757 High Gloss Impact Resistant ABS Particles
| Flexural Strength: | 70 MPa |
|---|---|
| Color: | White |
| Tensile Strength: | 50 MPa |
VIDEO
Chimei Polylac Pa-765a ABS Plastic Particles High Flow Flame Retardant V0 Grade
| Material: | ABS |
|---|---|
| Processing Method: | Injection Molding |
| Color: | Natural/White |
VIDEO
10% Glass Fiber Reinforced PC/ABS Particles High Strength
| Density (23°C): | 1.20 G/cm³ |
|---|---|
| Melt Volume-Flow Rate (MVR) (220°C/10.0 Kg): | 18 Cm³/10min |
| Flame Rating: | HB |
VIDEO
Laser Engraving PC ABS Particles Black Products Engraving White Words
| Density (23°C): | 1.18 G/cm³ |
|---|---|
| Melt Volume-Flow Rate (MVR) (220°C/10.0 Kg): | 20 Cm³/10min |
| Molding Shrinkage: | 0.50 To 0.70 % |
VIDEO
High Impact PC ABS Particles Natural Color Black High Gloss
| Density (23°C): | 1.15 G/cm³ |
|---|---|
| Melt Volume-Flow Rate (MVR) (220°C/10.0 Kg): | 25 Cm³/10min |
| Molding Shrinkage: | 0.50 To 0.70 % |
VIDEO
Flame Rating HB 25% PC Fiber Reinforced Polycarbonate Particles for Density 23°C and Durable Applications
| Density (23°C): | 1.35 G/cm³ |
|---|---|
| Melt Volume-Flow Rate (MVR) (220°C/10.0 Kg): | 18 Cm³/10min |
| Flame Rating: | HB |
VIDEO
Transparent Flame Retardant PC ABS Material UL94-V0 Injection Molding Grade
| Density (23°C): | 1.2 G/cm³ |
|---|---|
| Melt Volume-Flow Rate (MVR) (220°C/10.0 Kg): | 10 Cm³/10min |
| Flame Rating: | V0 |
VIDEO
Reinforced PC Flame Retardant V0 Fiber 30% PC GF30 V0 Black
| Density (23°C): | 1.39 G/cm³ |
|---|---|
| Melt Volume-Flow Rate (MVR) (220°C/10.0 Kg): | 20 Cm³/10min |
| Flame Rating: | V0 |