Petrothene® NA480178 LyondellBasell LDPE
| Density: | 0.923 G/cm³ |
|---|---|
| Melt Flow Rate (MFR) (190°C/2.16 Kg): | 0.25 G/10 Min |
| Processing Methods: | Extrusion, Blown Film |
Petrothene® NA480145 LyondellBasell LDPE
| Density: | 0.923 G/cm³ |
|---|---|
| Melt Flow Rate (MFR) (190°C/2.16 Kg): | 0.25 G/10 Min |
| Processing Methods: | Extrusion, Blown Film |
Petrothene® NA442051 LyondellBasell LDPE
| Density: | 0.923 G/cm³ |
|---|---|
| Melt Flow Rate (MFR) (190°C/2.16 Kg): | 1.5 G/10 Min |
| Processing Methods: | Extrusion, Blown Film |
Lupolen 2421d Lyondellbasell LDPE
| Tensile Strength At Yield: | 18MPa |
|---|---|
| Processing Temperature: | 160-200°C |
| Melt Index: | 0.25g/10 Min |
Lupolen 2426f Lyondellbasell LDPE
| Elongation At Break: | 800% |
|---|---|
| Vicat Softening Point: | 100°C |
| Tensile Strength At Yield: | 17 MPa |
Lupolen 2426h Lyondellbasell LDPE
| Tensile Strength At Yield: | 17.6 MPa |
|---|---|
| Processing Temperature: | 160-200°C |
| Melt Index: | 2 G/10 Min |
Lupolen 2420d Lyondellbasell LDPE
| Tensile Strength At Yield: | 17.5 MPa |
|---|---|
| Processing Temperature: | 160-200°C |
| Melt Index: | 2 G/10 Min |
Lupolen 2420h LyondellBasell LDPE
| Elongation At Break: | 800% |
|---|---|
| Vicat Softening Point: | 100°C |
| Tensile Strength At Yield: | 18 MPa |
Purell 3020d LyondellBasell LDPE
| Impact Strength: | No Break |
|---|---|
| Flexural Modulus: | 200 MPa |
| Tensile Strength: | 17 MPa |
Lupolen 2426K LyondellBasell LDPE
| Tensile Strength At Yield: | 17.8 MPa |
|---|---|
| Processing Temperature: | 160-200°C |
| Melt Index: | 4 G/10 Min |