Prime Polymer Evolue PE SP4030 Cast Film
| Melt Mass-Flow Rate (MFR): | 3.8 G/10 Min |
|---|---|
| Density: | 0.938 G/cm³ |
| Processing Method: | Cast Film |
Polyethylene LLDPE Granules Bio Based Sugarcane Braskem Green PE SLL318
| Density (23°C): | 0.918 G/cm³ |
|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 Kg): | 2.7 G/10 Min |
| Molding Temperature: | 170 -180 °C |
Braskem Green PE SLL118 Bio Based Sugarcane Polyethylene LLDPE Plastic Granules
| Density (23°C): | 0.916 G/cm³ |
|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 Kg): | 1 G/10 Min |
| Processing Method: | Blown Film Extrusion. |
Bio Based Sugarcane LLDPE Polyethylene Granules Braskem Green PE SLL118/21
| Density (23°C): | 0.918 G/cm³ |
|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 Kg): | 1 G/10 Min |
| Processing Method: | Blown Film ,Film Extrusion |
Bio Based Sugarcane Polyethylene LLDPE Granules Braskem Green PE SLH218
| Density (23°C): | 0.916 G/cm³ |
|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 Kg): | 2.3 G/10 Min |
| Processing Method: | Blown Film Extrusion. |
Prime Polymer Evolue Sp2120
| Melt Mass-Flow Rate (MFR): | 2.2 G/10 Min |
|---|---|
| Density: | 0.921 G/cm³ |
| Processing Method: | Blown Film |
Prime Polymer Evolue Sp3010 Blown Film
| Melt Mass-Flow Rate (MFR): | 0.8 G/10 Min |
|---|---|
| Density: | 0.926 G/cm³ |
| Processing Method: | Blown Film |
Talsox® 7200 Formosa Plastics Hdpe
| Density: | 0.955 G/cm3 |
|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 Kg) 0.05 G/10 Min: | 22 G/10 Min |
| Manufacturer: | Taiwan Formosa Plastics |
Talsox® 8001 Formosa Plastics Hdpe
| Density: | 0.948 G/cm3 |
|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 Kg) 0.05 G/10 Min: | 0.05 G/10 Min |
| Manufacturer: | Taiwan Formosa Plastics |
Prime Polymer Evolue SP2040 Cast Film Mlldpe
| Melt Mass-Flow Rate (MFR): | 3.8 G/10 Min |
|---|---|
| Density: | 0.918 G/cm³ |
| Processing Method: | Cast Film |